Abstract
Polyelectrolyte multilayer coatings were prepared from solutions of poly(methacrylic acid) and poly-l-histidine. Bone morphogenetic protein 2 (BMP-2) was adsorbed onto the surface of anodized titanium and polyelectrolyte multilayer coatings were built up on top of the BMP-2. The effect of deposition conditions on coating properties and preosteoblast response was measured by comparing coatings prepared under natural conditions to those prepared from solutions at pH = 6.0 and solutions containing 0.1 M NaCl. High levels of BMP-2 release were achieved, with coatings prepared from pH = 6.0 solutions releasing 86 ng cm-2 and coatings prepared from solutions containing 0.1 M NaCl releasing 114 ng cm-2 over 25 days. Enhanced preosteoblast differentiation was observed on coatings prepared from modified solutions; however, this increased differentiation was apparent for BMP-2-eluting and control coatings. Additionally, a positive relationship between surface roughness and differentiation was observed, which may account for increased differentiation for systems that do not release BMP-2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.