Abstract
Abstract The feasibility of applying an innovative process to manufacture composite decking boards with quartersawn or starsawn southern pine lumber bonded with phenol resorcinol formaldehyde (PRF) and polyurethane (PU) adhesives was studied. It was feasible to make quatersawn-based composite decking panels with possible improved surface qualities. Accelerated aging tests showed that composite quartersawn decking samples were more resistant to aging than flatsawn decking samples in terms of shear strength, especially after exposure to 12 wet–dry aging cycles. Compared with the PRF adhesive, the PU adhesive resulted in greater initial dry shear strength but had lower shear strength after the accelerated aging test. Furthermore, the amount of wood failure increased for the PRF-bonded samples and decreased for the PU-bonded samples after accelerated aging tests. Compared with solid quartersawn decking boards, the quartersawn composite decking boards had the same modulus of rupture and modulus of elasticity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.