Evaluation of the Effect of the Loading Time on the Microtensile Bond Strength of Various Restorative Materials Bonded to Silver Diamine Fluoride-Treated Demineralized Dentin.

Abstract

The aim of this study was to evaluate the effect of immediate versus delayed loading times on the microtensile bond strength (μTBS) of restorative materials, including resin-based composite (RBC), resin-modified glass ionomer cement (RMGIC) and glass ionomer cement (GIC), that were bonded to silver diamine fluoride (SDF)-treated demineralized dentin. Ninety caries-free extracted premolar teeth were assigned to three groups (n = 30) loaded with RBC, RMGIC and GIC restorative materials. Each group was further divided into three subgroups (n = 10): subgroup A (control specimens), immediate loading of the restorative material on sound dentin; subgroup B, demineralized dentin, SDF treatment and immediate loading of the restorative material; and subgroup C, demineralized dentin, SDF treatment and restorative material loading a week later. One-way ANOVA and Tukey’s post-hoc tests were performed to compare the μTBS values. The RBC exhibited the highest µTBS, followed by RMGIC and GIC. Multiple comparisons showed an increase in the µTBS in the delayed loading groups irrespective of the restorative material used. The majority of the failure modes were adhesive. Delayed loading of RMGIC for 1 week after SDF application showed significantly higher µTBS than that of immediate loading.