Evaluation of the effect of diode laser activation on push-out bond strength of different intraorifice barriers in endodontically treated teeth. An in-vitro study

Abstract

Introduction: The placement of intraorifice barriers should facilitate proper adhesion; however, it is still a challenge with existing intraorifice barrier materials. Thus, this study aims to evaluate the push-out bond strength of Glass Ionomer Cement (GIC), Tetric-N-Flow, and Biodentine as intraorifice barriers with and without diode laser activation. Materials and Methods: Human-extracted single-rooted 60 mandibular premolars were decoronated to standardize 13 mm root length. Root canal was instrumented with rotary ProTaper universal system till F4 and alternatively irrigated with 5 ml of 2.5% sodium hypochlorite and normal saline, followed by obturation using gutta-percha and AH-plus sealer. About 3.5 mm of gutta-percha was removed from the orifice using peso reamer. Horizontal tooth sections of 3.5 mm in length were obtained from the coronal third of each sample and were randomly divided into three groups (n = 20 each) for intraorifice barrier materials. Group 1: GIC; group 2: Tetric-N-Flow and group 3:Biodentine. Each group was further subdivided into two subgroups A and B (n = 10 each) with and without diode laser. After 7 days, the specimens were mounted in acrylic molds and push-out bond strength was evaluated under universal testing machine. Data analysis was done using One way-analysis of variance and post hoc Tuckey comparison tests (P ≤ 0.05). Results: Laser activation in each group showed greater push-out bond strength; however, Biodentine with laser (group 3A) exhibited higher bond strength compared to all groups (P ≤ 0.05). Conclusion: Biodentine with laser activation before placement of the coronal barrier of endodontic treated tooth increases the quality of bond strength.