Abstract
The extent of subsurface damage on (0001) GaN wafers post different polishing treatments was quantified using depth-resolved cathodoluminescence spectroscopy (DRCLS). The band edge emission spectra were obtained from CLS with different electron energies, which manifested a significant non-radiative recombination resulted from polishing-induced subsurface damage. Cross-sectional transmission electron microscopy (XTEM) was also used to diagnose the extent of the subsurface damage layer. For the GaN polished with 1.00 and 0.25 μm diamonds abrasive, the extent of non-radiative subsurface damage is about 250 and 100 nm, corresponding to the calculated electron penetration depth at the accelerating voltage for the onset of band edge emission. In this study, the depth of subsurface damage estimated from CL spectra compared well with direct XTEM measurements in GaN substrate.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.