Abstract
Proton-conducting solid oxide fuel cells (H+-SOFCs) have attracted considerable interest recently. However, the overall cell performance of H+-SOFCs is still low due to the lack of a promising cathode material. In this study, SrSc0.175Nb0.025Co0.8O3-δ (SSNC) was synthesized for evaluation as a cathode material in H+-SOFCs based on a BaZr0.1Ce0.7Y0.2O3-δ (BZCY) electrolyte. The chemical compatibility and stability of the SSNC cathode with the BZCY electrolyte in humidified air were studied. In addition, the electrochemical behavior of the SSNC cathode on the BZCY electrolyte was investigated using SSNC/BZCY/SSNC symmetrical cells at 600 °C in dry air and humidified air at various H2O partial pressures. Promising electrocatalytic activity was observed for the SSNC cathode in humidified air. The area specific resistance obtained on symmetrical cells at 600 °C in a 10% H2O-air atmosphere was 0.26 Ω cm2. A promising peak power density of 498 mW cm−2 was obtained using an anode-supported cell with a 46 μm-thick BZCY electrolyte layer at 700 °C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.