Evaluation of Shear Bond Strengths of 3D Printed Materials for Permanent Restorations with Different Surface Treatments.

Abstract

The development of high-filled 3D printing resin necessitates a bonding protocol for dental indirect restorations to achieve optimal bond strength after cementation. This study evaluates shear bond strengths of high-filler 3D printed materials for permanent restorations with various surface treatments. Rodin Sculpture 1.0 (50% lithium disilicate fillers) and 2.0 Ceramic Nanohybrid (>60% zirconia and lithium disilicate fillers) were tested, with Aelite All-Purpose Body composite resin as control. Samples were prepared, post-cured, and sandblasted with alumina (25 µm). Surface roughness was analyzed using an optical profilometer. Two bonding protocols were compared. First, groups were treated with lithium disilicate silane (Porcelain Primer) or zirconia primer (Z-Prime Plus) or left untreated without a bonding agent. Beam-shaped resin cement (DuoLink Universal) specimens were bonded and stored in a 37 °C water bath. Second, additional sets of materials were coated with a bonding agent (All-Bond Universal), either followed by silane application or left untreated. These sets were then similarly stored alongside resin cement specimens. Shear bond tests were performed after 24 h. SEM images were taken after debonding. One-Way ANOVA and post hoc Duncan were performed for the statistical analysis. Rodin 1.0 exhibited increased adhesive failure with silane or zirconia primer coating, but significantly improved bond strengths with bonding agent application. Rodin 2.0 showed consistent bond strengths regardless of bonding agent application, but cohesive failure rates increased with bonding agent and filler coating. In all groups, except for Rodin 1.0 without bonding agent, silane coating increased cohesive failure rate. In conclusion, optimal shear bond strength for high-filler 3D printing materials can be achieved with silane coating and bonding agent application.