Evaluation of Residual Stress Development at the Interface of Plasma Electrolytically Oxidized and Cold-Worked Aluminum

Abstract

Fatigue failure in hard oxide-coated aluminum is usually driven by rapid short crack propagation from the interface through the substrate; mitigation of this is possible by introducing interfacial compressive stresses. Combining cold work with hard oxide coating can improve their performance under conditions of simultaneous wear, corrosion, and fatigue. Three-dimensional strain fields in an aluminum alloy with combined cold work and PEO coating have been measured and mechanisms for stress redistribution presented. These comprise material consumption, expansive growth of oxide layers, and local annealing.