Abstract
This study aims to evaluate the microstructure and mechanical behavior of aluminum 2024 and stainless steel 304 dissimilar joints. The gas tungsten arc welding (GTAW) process has been employed to weld base metals by inserting copper-nickel-based (Cu-10%Ni) filler metal. The effects of GTAW parameters such as welding current, welding speed, and gas flow on microstructure and tensile strength have been analyzed through the Taguchi method. Results revealed that tensile strength is primarily influenced by welding current, followed by speed and gas flow rate. The excellent joint strength of 138 MPa has been achieved by using Cu-10%Ni filler metal. The optimal combination of parameters, i.e., welding current of level 2 (80 A), welding speed of level 1 (100 mm/min), and gas flow rate of level 3 (10 l/min), has been obtained through SN ratio optimization. Microstructure and EDS analysis depicted that the weld zone of a high-strength joint contained fine dendrites and CuAl and NiAl solid solutions, while the weld zone of a low-strength joint featured coarse dendrites and brittle FeAl phases.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.