Abstract
The microhardness, surface roughness and wear resistance of different types of resin composites, polymerized by a Quartz Tungsten Halogen (QTH) or Light Emitting Diode (LED) light curing units (LCU) were evaluated in this in vitro study. Cylindrical blocks were prepared from composites (8 mm in diameter, and 2 mm in thickness) and polymerized by a LED or a QTH LCU. Vickers hardness was measured on the top and bottom surfaces of the specimens. Surface roughness was measured with a surface profilometer on the top of the specimens. For the wear test, specimens were tested in a conventional pin-on-disc tribology machine under 15 N loads. The statistical analyses were performed by one-way analysis of variance (ANOVA) and t-tests, including the Bonferroni correction. Nanocomposite material Clearfil Majesty Posterior showed the highest hardness values in all polymerization types at the top and bottom surfaces (p < 0.05). Microhybrid Clearfil APX and hybrid Quixfil composites demonstrated the greatest surface roughness. Wear resistance of Clearfil Majesty Posterior was found to be the highest among the other tested resin composites. The results indicated that Clearfil Majesty Posterior demonstrated higher microhardness, less surface roughness, and higher wear resistance when compared with the other tested materials for both polymerization types.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Biomedical Materials Research Part B: Applied Biomaterials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.