Abstract
Some novel composites were prepared with polyamide 6(PA6) filled with wollastonite particles and wollastonite inorganic modified by aluminium silicate composite materials (WIMS) as fibrous fillers. Subsequently, these composites were investigated for tensile, charpy notched impact, bending strength, bending modulus and heat distortion temperature, and the mechanism of PA6 reinforced by WIMS was discussed through SEM photos of wollastonite and WIMS and the current two most popular equations: Pukanszky equation and Nielsen equation.The results show that the PA6 products filled with WIMS have superior mechanical properties(tensile strength 71.65Mpa, bending strength 106.61Mpa, bending modulus 3258.22Mpa) than that of uncoated wollastonite and pure PA6, and the heat distortion temperature increases by 88.6°C than pure PA6 and 17.2°C than wollastonite. Inorganic modification of wollastonite can improve the joint interface between wollastonite and PA6, thus improving their mechanical properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.