Abstract
Evaluation of hillock-like deposition behaviour of WC/Co coatings was performed using a rotary shutter procedure coupled with 100 passes of high velocity oxy fuel thermal spraying. During the spraying procedure, a DPV 2000 in situ diagnostic instrument was used to monitor the temperature and velocity of inflight particles. The microstructure of the coatings was analysed using an optical microscope to monitor the porosity and thickness distributions at various positions of the hillock-like coatings. A 7·1% porosity was observed at the centre of the hillock-like coatings, and a 10% porosity was observed at the edge, each at a spraying distance of 200 mm. The centre area of hillock-like coatings exhibited almost a 30% decrease in porosity compared to the edge area. The results indicate a higher quality structure at the centre area of the hillock-like coatings.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.