Abstract
ObjectivesThe aim was to assess how incorporating a short-fiber composite (SFC) core would affect the fracture behavior of direct and indirect overlays. Furthermore, to examine the relationship between the thickness ratio of SFC core to particulate-filled composite (PFC) veneering and the fracture-behavior of bilayered-structured restorations.Materials and methodsA total of 120 molars were used to create MOD cavities, with palatal cusps removed. Four different groups of direct overlays were then made (n = 15/group), all of which featured a SFC core (everX Flow) with varying thicknesses (0, 1, 4, and 5 mm), as well as a surface layer of PFC (G-aenial Posterior), with the overall thickness of the bilayered-structured restoration set at 5 mm. Additionally, four groups of CAD/CAM restorations were created (Cerasmart 270 and Initial LiSi Block), with or without 2 mm of SFC core reinforcement. Following the fabrication of these restorations, cyclic fatigue aging was carried out for a total of 500,000 cycles, with an applied maximum load (Fmax) of 150 N. Subsequently, each restoration underwent quasi-static loading until fracture. The fracture mode was subsequently evaluated using optical microscopy and SEM.ResultsThere were no statistically significant differences (p > 0.05) observed in the fracture resistance of indirect overlays reinforced with a 2-mm SFC core compared to those made solely from restorative materials. Direct overlays constructed using plain SFC or with a 4-mm layer thickness of SFC core exhibited significantly higher fracture resistance values (2674 ± 465 and 2537 ± 561 N) (p < 0.05) when compared to all other groups tested, according to the statistical analysis ANOVA.ConclusionsThe most effective method for restoring large MOD cavities was found to be direct restoration using SFC either alone or as a bulk core in combination with PFC composite.Clinical relevanceThe use of SFC as bulk reinforcing base will significantly improve the loading performance of directly layered restorations.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.