Abstract
Austenitic stainless steel (JIS-SUS304L) with a bimodal harmonic structure, which is defined as a coarse-grained structure surrounded by a network of fine grains, was fabricated using powder metallurgy to improve both the strength and ductility. Four-point bending fatigue tests and K-decreasing tests were conducted in air at room temperature under a stress ratio R of 0.1 to investigate fatigue crack propagation in SUS304L. The fatigue limit of this harmonic-structured material was higher than that of the material with a homogeneous coarse-grained structure. This is attributable to the formation of fine grains by mechanical milling and to the suppression of pore formation. In contrast, the threshold stress intensity range, DKth, for the harmonic-structured material was lower than that for the homogeneous coarse-grained material, while the crack growth rates, da/dN, were higher at comparable DK. These results can be attributed to a reduction in the effective threshold stress intensity range, DKeff,th, due to the presence of fine grains in the harmonic structure.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.