Abstract
In multi-layered films on a silicon substrate for an advanced electronics devices, interfacial fracture often takes place and its strength (thin film adhesion) is very important in reliability. This study aims that the mechanism of damage initiation during nanoscratch test is examined for Si3N4/Cu/TaN films on a silicon substrate. In the case that the interfacial strength is weak, the interfacial damage initiates before surface film failure. In the case of edge-forward scratching, there are little effects of the rates of normal stress and scratching on the critical load. Contact analysis without friction for the system consisting of the tip, films and substrate reveals that the peak of shear stress appears on the track near the tip. Face-forward scratching shows the same behavior of damage as edge-forward scratching. Stress states acting on the interface in scratch tests suggest that the damage initiates when shear stress reaches the critical value.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.