Abstract
Rechargeable Zn/MnO2 alkaline batteries are a promising technology for grid storage applications since they are safe, low cost, and considered environmentally friendly. Here, a commercial ceramic sodium ion conductor which is impervious to zincate [Zn(OH)42−], a contributor to MnO2 cathode failure, is evaluated as the battery separator. As received, the ionic conductivity of this separator was measured with electrochemical impedance spectroscopy to be 3.5 mS cm−1, while its thickness is 1.0 mm, resulting in large total membrane resistance of 25.3 Ω. Reducing the thickness of the ceramic to 0.5 mm provided for a decreased resistance of 9.8 Ω. Crossover experiments conducted using inductively coupled plasma - mass spectrometry measurements failed to measure any Zn(OH)42− transport indicating a diffusion coefficient that is at least two orders of magnitude less than that for the commercial cellophane and Celgard separators. For 5% DOD at a C/5 rate, the cycle lifetime was increased by over 22% using the 0.5 mm thick ceramic separator compared to traditional Celgard and cellophane separators. Scanning electron microscopy/energy dispersive X-ray spectroscopy and X-ray diffraction characterization of cycled electrodes showed limited amounts of zinc species on the cathode utilizing the ceramic separator, consistent with its prevention of Zn(OH)42− transport.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.