Abstract
The Ni-based cermet Solid Oxide Fuel Cell (SOFC) anode is prone to poisoning by sulfur-based odourising agents, and naturally occurring sulfur species, present in unprocessed natural gas feeds. Next generation SOFC anodes should be able to withstand exposure to these poisons in the event of a malfunction or breakdown of desulfurisation units. Here, we present results pertaining to the sulfur-tolerance of Ni/Ce0.80Gd0.20O1.90 (CGO), Pt/CGO and Rh/CGO co-impregnated La0.20Sr0.25Ca0.45TiO3 anode ‘backbone’ microstructures and their ability to recover performance after being exposed to H2S. The Ni/CGO co-impregnated system exhibited severe poisoning by H2S, however, the Rh/CGO system displayed good stability in Area Specific Resistance (ASR) upon introduction of 1–2 ppm of H2S and the Pt/CGO system showed minimal increases in ASR with the addition of 1–8 ppm H2S. Recovery measurements performed in non-humidified H2 at 300 mA cm−2, after exposure to 8 ppm H2S, indicated that the Pt/CGO and Rh/CGO systems could recover within 10 min, whilst 60 min were required to achieve almost a full recovery of performance for the Ni/CGO system. Additionally, all three impregnate systems showed good stability in operating voltage, after an initial drop, in a fuel gas containing simulated syngas (2:1 H2:CO) with 8 ppm H2S.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.