Abstract
Experiment is looking at the influence of dimensions, heat treatment temperature and cooling media effect linearly on hardness, tensile strength steel AISI 4140 so that the level comparison of the hardness of influence on the diameter variation (input effects the response). The Full Factorial Design of Experiment Method is used to assess the results of the hardness test in accordance with the testing hypothesis. Design of Experiment (DOE) has been widely used to determine design factors that significantly influence target responses and build empirical models that represent relationships between significant factors. Reviewing the literature revealed that the majority of researchers explored various DOE . Response Tempering heat treatment with Quenching Oil media, this study used AISI 4140 material with a diameter of 29 mm, 33 mm and 35 mm. Results AISI 4140 of commercial production by partial cutting are then taken for hardness testing. The Full Factorial Design of Experiment Method is used to assess the results of the hardness test in accordance with the hypothesis according to the analysis of variance(Anova) . The response of the hardness test data input in the 30 0 & 90 0 direction is not influenced by the AISI 4140 material dimensions and the direction of the test surface data retrieval. Fo, 5%, 2.15 = 3.68, then Fo = 50.11> 3.68 in the 30 0 test direction and Fo, 5%, 2.15 = 3.68, then Fo = 70.79> 3, 68, in the 90 0 test direction where H0 cannot be accepted while H1 is accepted.
Highlights
Proses produksi pada industri baja yang memproduksi produk sesuai spesifikasi standard terkadang proses produksinya perlu dilakukan proses quality control secara keseluruhan dan untuk penggunaan kekhususan perlu dilakukan proses tempering produk komersial untuk mendapatkan spesifikasi yang diinginkan
Experiment is looking at the influence of dimensions
The Full Factorial Design of Experiment Method is used to assess the results of the hardness test in accordance
Summary
Hasil uji tarik AISI 4140 Hasil pengujian tarik dengan tensile test machine untuk pengambilan data diameter 29 mm, 33 mm dan 35 mm material AISI 4140 setelah dilakukan perlakuan panas quench tempering dengan standard pengujian ASTM E9 sesuai Tabel 3.1. Tabel 3.1 dan gambar 3.1 menunjukan adanya peningkatan stress yield dengan peningkatan dimensi diameter material sedangkan reduction area dan elongation adanya penurunan dengan bertambahnya dimensi diameter material
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have