Abstract
Al Ni, Al Mn and Al Zn dilute alloys were studied by low angle X ray diffraction, in order to determine if the solute is really dispersed. For obtaining the best dissolution, Al Ni and Al Mn were rapidly quenched from the melt, and Al Zn was quenched from an homogenization temperature. The regrouping rate is small for Al Zn and Al Mn, while Al Ni always shows variable dimension heterogeneities. In all cases, the structure evolves rapidly by annealing at temperature higher than 300°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.