Abstract
In this work, we present a novel binary solvent of ethylene glycol/water medium (W/EG 50:50) that play an important role in the formation of the hierarchical meso-structures of bow-tie-like composition units composed of self-assembly lithium iron phosphate (LFP) nano-sheets. Citric acid uses as inorganic carbon source and no other surfactant or template agent is applied. Results show that the crystallinity and the size of the particles depend on the nature of the solvent used. TEM results show that the sample prepared in ethylene glycol (EG-LFP/C) consists of well-distributed nanoparticles of size approximately 50 nm in diameter, which is uniformly embedded in thin carbon layers. The EG-LFP/C composite delivers the first discharge capacity of 166 mAh g−1, i.e. 97.6% of the theoretical capacity, when tested under a discharge rate of 0.1C. This material shows specific discharge capacities as high as 114 mAh g−1 at 10C rates and exhibits a long-term cycling stability with a capacity loss of only 1.4% after 100 cycles. The high rate performance could be attributed to the amount and/or the quality of the thin carbon coating, improved crystallinity as well as high specific surface area and porosity induced by the special bow-tie-like mesostructures.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have