Abstract
Plasma-sprayed thermal barrier coatings (TBCs) are applied to protect the blades of a gas turbine system from high-temperature gas and to lower the surface temperature of the blades. The failure of TBC is directly connected to the failure of the blades because the spallation of a ceramic layer leads to the acceleration of local corrosion and oxidation at the location of failure. Therefore, the spallation life of TBC is very important in the evaluation of the reliability of a gas-turbine blade.In this study, thermal fatigue tests were performed at 1100°C and 1151°C. Then, c-scanning and bond strength tests were performed for TBC specimens that were thermally aged by thermal fatigue tests. From the results, an empirical equation based on the ratio of the delamination area and the thermal cycle number was presented and the spallation life of a TBC specimen could be roughly estimated using the relationship between the delaminated area and the number of cycles.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call