Abstract
Dislocations would be induced after plastic deformation, which might change the mechanical properties of solids. FeCrNi austenitic model alloy and its Mo-diluted alloy were cold rolled with different degree of thickness reduction. Positrons are sensitive to point defects, which are easily trapped and annihilated around the trapping sites. The mean positron lifetimes have been used to estimate the average dislocation concentration in solids. Meanwhile, the trapping efficiency μ was calculated from the lifetime results. The trapping efficiency value is estimated about 3.31×10-7 cm3s-1 for FeCrNi alloy and 3.31×10-7 cm3s-1 for Mo-diluted alloy, respectively. The increment of the hardness value during plastic deformation is related to the increase of the dislocation density and dislocation pile up in solids.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.