Abstract
A three-dimensional micromechanics framework is developed to estimate the mode I through-thickness intralaminar crack resistance curve of unidirectional carbon fibre-reinforced polymers. Finite element models of geometrically-scaled single edge notch tension specimens were generated. These were modelled following a combined micro-/meso-scale approach, where the region at the vicinity of the crack tip describes the microstructure of the material, while the regions far from the crack tip represent the mesoscopic linear-elastic behaviour of the composite. This work presents a novel methodology to estimate fracture properties of composite materials by combining computational micromechanics with the size effect method. The size effect law of the material, and consequently the crack resistance curve, are estimated through the numerically calculated peak stresses. In-depth parametric analyses, which are hard to conduct empirically, are undertaken, allowing for quantitative and qualitative comparisons to be successfully made with experimental and numerical observations taken from literature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Composites Part A: Applied Science and Manufacturing
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.