Establishment and inactivation of mono-species biofilm in a semipilot-scale water distribution system using nanocomposite of silver nanoparticles/montmorillonite loaded cationic chitosan

Abstract

This study presents a novel approach in the synthesis and characterization of nanocomposites comprising cationic chitosan (CCS) blended with varying concentrations of silver nanoparticles/montmorillonite (AgNPs/MMT). AgNPs/MMT was synthesized using soluble starch as a reducing and stabilizing agent. Subsequently, nanocomposites, namely CCS/AgMMT-0, CCS/AgMMT-0.5, CCS/AgMMT-1.5, and CCS/AgMMT-2.5, were developed by blending 2.5 g of CCS with 0, 0.5, 1.5, and 2.5 g of AgNPs/MMT, respectively, and the corresponding nanocomposites were prepared using ball milling technique. Transmission electron microscopy (TEM) analysis revealed the formation of nanocomposites that exhibiting nearly spherical morphologies. Dynamic light scattering (DLS) measurements displayed average particle sizes of 1183 nm, 131 nm, 140 nm, and 188 nm for CCS/AgMMT-0, CCS/AgMMT-0.5, CCS/AgMMT-1.5, and CCS/AgMMT-2.5, respectively. The narrow polydispersity index (~0.5) indicated uniform particle size distributions across the nanocomposites, affirming monodispersity. Moreover, the zeta potential values exceeding 30 mV across all nanocomposites that confirmed their stability against agglomeration. Notably, CCS/AgMMT-2.5 nanocomposite exhibited potent antibacterial and antibiofilm properties against diverse pipeline materials. Findings showed that after 15 days of incubation, the highest populations of biofilm cells, Pseudomonas aeruginosa biofilm, developed over UPVC, MDPE, DCI, and SS, with corresponding HPCs of 4.79, 6.38, 8.81, and 7.24 CFU/cm2. The highest cell densities of Enterococcus faecalis biofilm in the identical situation were 4.19, 5.89, 8.12, and 6.9 CFU/cm2. The nanocomposite CCS/AgMMT-2.5 exhibited the largest measured zone of inhibition (ZOI) against both P. aeruginosa and E. faecalis, with measured ZOI values of 19 ± 0.65 and 17 ± 0.21 mm, respectively. Remarkably, the research indicates that the youngest biofilm exhibited the most notable rate of inactivation when exposed to a dose of 150 mg/L, in comparison to the mature biofilm. These such informative findings could offer valuable insights into the development of effective antibiofilm agents and materials applicable in diverse sectors such as water treatment facilities, medical devices, and industrial pipelines.