Abstract
AbstractIn this investigation, the main objective was to study the mechanical properties of alternating poly(propylene carbonate) copolymer (PPC). The PPC used in this study was derived from propylene oxide and carbon dioxide using zinc glutarate as catalyst. The molecular weight of the PPC copolymer used in this study has M̄n∼33,000. The synthesized PPC was compression molded into sheets of thickness ∼1mm. The fracture toughness of the PPC films was determined using the essential work of fracture (EWF) technique, at a laboratory temperature of 20°C, and a loading rate of 1 mm/min. During the EWF measurement, a significant amount of plastic deformation has taken place around the initial ligament region. The measured specific total fracture work (wf) was observed to vary in a linear fashion with the specimen ligament (l), and hence satisfied the basic requirement for EWF analysis. The specific essential fracture work (we) for the PPC film was measured to be 11.0 kJ/m2. The PPC showed a prominent recovery behavior. The severely deformed region surrounding the fracture ligament was observed to recover completely 8 days after fracture testing. Polym. Eng. Sci. 44:580–587, 2004. © 2004 Society of Plastics Engineers.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.