Abstract
Zn–Al–NO 3–LDH was synthesized using the co-precipitation method at pH 7±0.1 and ratio Zn/Al=4. The heat treatment of LDH was studied by X-ray diffraction (XRD) and thermogravimetric analysis (TGA/DTG) to investigate the stability of the LDH structure. The in situ electron spin resonance (ESR) spectra of fresh LDH from room temperature up to 190 °C were obtained, which are due to the presence of nitrate radicals in LDH interlayer. ESR spectra of sintered LDH below 200 °C (ex situ ESR spectra) were investigated, which are also due to the nitrate radicals. However, at 200 °C and above, spectra were due to the oxygen vacancies of ZnO, which was formed during the thermal treatment of LDH. Thermal diffusivity of LDH as a function of in situ temperatures results in a nonlinear relation, which is due to the changing water content of LDH when temperature increases. However, thermal diffusivity of LDH as a function of sintered temperatures showed a linear relation and the slope of these data demonstrated the dependency between thermal diffusivity and water content of LDH below 200 °C. For temperature above 180 °C, the thermal diffusivity behavior was mainly due to the ZnO phase in LDH.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.