Abstract
A Co-Pd film was deposited on 316L stainless steel by electroplating. The erosion–corrosion behavior of the Co-Pd plated samples in hot sulfuric acid solution with SiO2 particles was investigated. The results showed that there was a significant synergistic effect between erosion and corrosion. At higher stirring speed, even in such strong corrosive environment the erosion–corrosion rate of Co-Pd plated samples was controlled mainly by the erosion resistance. The erosion–corrosion resistance of pure Pd plated sample decreased rapidly with increasing stirring speed, whereas that of Co-Pd plated sample kept almost stable under the tested conditions due to the high micro-hardness and good corrosion resistance of the film.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.