Abstract
The present study establishes an experimental platform for investigating arc erosion and explores the erosion characteristics of Ti3AlC2 material under a voltage of 10 kV in SF6/N2, SF6/CO2, and N2/CO2 environments. Our findings reveal that the arc energy and duration exhibit a gradual increase in the sequence of SF6/N2, SF6/CO2, and N2/CO2, while the breakdown strength decreases. Scanning electron microscopy (SEM) and a three-dimensional laser confocal microscope were employed to observe uneven erosion morphology. Additionally, high-speed camera footage captures the arc bending and drifting phenomenon caused by Rayleigh-Taylor instability between the arc and gas. X-ray diffraction (XRD), Raman spectroscopy, and X-ray photoelectron spectroscopy (XPS) analysis were utilized to characterize the composition of eroded surfaces. Erosion models were proposed for each mixed atmosphere along with comprehensive discussions on their underlying mechanisms. This work expands the application scope of MAX phase materials while providing a theoretical foundation for designing electrical contact materials.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.