Abstract
AbstractThe factors affecting optical gain were studied for Er-doped BaTiO3 thin film waveguides. Er-doped BaTiO3 with dopant concentrations of 0.3 – 9 at.% was deposited by metal-organic chemical vapor deposition. The luminescence efficiency was maximized by optimizing the growth temperature and erbium concentration as well as by post-deposition annealing. Stimulated emission was studied using the pump-probe technique over the spectral range of 1,520-1,550 nm. A maximum differential gain of 3 dB/cm was measured at 1,540 nm in an 8 mm long, 8 μm wide ridge waveguide.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.