Abstract
In order to obtain essential information on the formation process of the high-Tc phase in the Bi, Pb-Sr-Ca-Cu-O system, phase equilibria in the system PbO-CaO-CuO have been studied, mainly by x-ray diffraction analysis and thermal analysis. Temperature versus composition diagrams were established for the systems PbO-CuO(Cu2O) and PbO(PbO2)–CaO in air. Three invariant points were detected in these systems: a eutectic reaction (PbO + Ca2PbO4 = L) at 847 ± 6°C, a peritectic reaction (Ca2PbO4 = L + CaO) at 980 ± 2°C, and a eutectic reaction (PbO + CuO = L) at 789 ± 3°C. For the system PbO(PbO2)-CaO-CuO, subsolidus phase equilibrium in air was established. The liquidus was also examined at 780, 800, and 820°C, and a ternary (PbO-Ca2PbO4-CuO) eutectic point was detected at 772 ± 6°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.