Equilibration of plain carbon and alloy steels with endothermic carburizing atmospheres: Part II. Oxidation of plain carbon and Armco steels during carburizing at 1000 °C and 1038 °C

Abstract

Carbon contents by the weight gain of AISI type 1010 steel foils equilibrated with CO-CO2 mixtures at 1000 °C were 0.03 wt.% to 0.07 wt.% higher than those by chemical analysis at carbon potentials of 0.2 wt.%C to 0.7 wt.%C. The lower the carbon potential, the bigger the difference became. This difference of 0.05 wt.% to 0.08 wt.% was also measured when the same materials were equilibrated with CO-CO2 mixtures at 1038 °C at carbon potentials below 0.4 wt.%C. Oxygen analyses of these equilibrated steel foils confirmed that those differences of 0.03 wt.% to 0.07 wt.% and 0.05 wt.% to 0.08 wt.% were mainly due to the selective oxidation of manganese. When Armco steels and type 1010 steels were equilibrated simultaneously with endothermic-base carburizing atmospheres at 1038 °C, oxidation was negligible and the carbon contents of the both steels were identical at carbon potentials of 0.2 wt.%C to 1.4 wt.%C.