Abstract
The epoxy resins are very popular and plentifully used synthetic resins. The bisphenol A-based (DGEBA) and bisphenol F-based epoxy resins (DGEBF) crystallization is phenomenon which is for that kind of resins natural. They are undercooled liquids and they tend to form the crystal structure at the ambient temperature. The subject of the research is to determine the effect of some crystallinity of DGEBF on chosen mechanical parameters. The degree of crystallinity was counted through the specific weights of crystallized bisphenol F-based epoxy resins. The prepared crystallized samples of DGEBA/DGEBF mixtures were mixed in appropriate weight ratio with isophorondiamine (IPD) based curing agent. Measured was hardness Shore D according to EN ISO 868 standard and tensile parameters according to EN ISO 527-1 standard. Furthermore, the effect of crystallinity on chosen mechanical parameters was observed. It was found out that with the higher crystallinity maximum tensile stress and hardness increased close to the standard parameters amorphous DGEBA and DGEBF.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.