Abstract
Flexible copper conductors have been extensively utilized in flexible and wearable electronics. They can be fabricated by using a variety of patterning techniques such as vacuum deposition, photolithography, and various printing techniques. However, vacuum deposition and photolithography are costly and result in material wastage. Moreover, traditional printing inks require posttreatment, which can damage flexible substrates, or grafting polymers, which involve complex processes to adhere to flexible substrates. Therefore, this study proposes a facile method of fabricating flexible metal patterns with high electrical conductivities and remarkable bonding forces on a diverse range of flexible substrates. Catalytic ink was prepared by using a mixture of epoxy resin, copper nanopowder, and nanosilica. The ink was applied to a variety of flexible substrates, including a poly(ethylene terephthalate) (PET) film, polyimide film, and filter paper, using screen printing to establish a bridge layer for subsequent electroless deposition (ELD). The catalytic efficiency was significantly improved by treating the cured ink patterns with air plasma. The fabricated flexible metals exhibited excellent adhesion and desirable electrical conductivity. The sheet resistance of the copper layer on the PET substrate decreased to 9.2 mΩ/□ after 150 min of ELD. The resistance of the flexible metal on the PET substrate increased by only 3.125% after 5000 bending cycles. The flexible metals prepared in this study demonstrated good foldability, and the samples with filter paper and PET substrates failed after 40 and 70 folds, respectively. A pressure sensor with a bottom electrode consisting of a copper interdigital electrode on a PET substrate displayed favorable sensing performance.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.