Abstract
Abstract A novel type of aramid fibers coated with poly(ethylene glycol) methyl ether (PEGME)-modified multi-walled carbon nanotubes (MWCNTs) was designed using electrophoresis. Owing to the good interaction of MWCNT-PEGME with the matrix, the coated fibers were well dispersed in epoxy resin. Thin films of epoxy/aramid-MWCNT-PEGME were prepared by placing the modified aramid fibers in molds, and the epoxy resin was infused into them. 4,4′-Diaminodiphenylmethane was dissolved in epoxy before the resin was poured over the aramid fibers coated with MWCNT-PEGME. According to fracture surface studies, the modified fibers were completely miscible with the epoxy resin and the filler was dispersed well in the space between the aramid fibers. The tensile strength of neat resin was increased from 658 to 1198 MPa in 40 wt.% of fiber-loaded epoxy/aramid-MWCNT-PEGME 40 composite. The maximum flexural strength was also found to be higher for epoxy/aramid-MWCNT-PEGME 40 (1593 MPa). The glass transition temperature (T g) was studied using differential scanning calorimetry, in the range of 164–173°C. The tensile strength, modulus, flexural strength, and T g of epoxy/aramid fiber composites with unmodified fibers were found to be lower than those of epoxy/aramid-MWCNT-PEGME composites.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.