Abstract
ABSTRACTEpoxide‐terminated hyperbranched polyether sulphones (EHBPESs) with different backbone structures were synthesized and used as tougheners for diglycidyl ether of bisphenol‐A (DGEBA) curing system, which result in nonphase‐separated cured networks. Effects of backbone structure (at comparable degree of polymerization) and loading contents on the mechanical and thermal properties of cured hybrids were investigated. The hybrid containing EHBPES3, which has the most flexible backbone, shows the best mechanical performance and highest glass transition temperature (Tg). Compared with unmodified system, the impact strength, tensile strength, elongation at break of the hybrid containing 5% EHBPES3 increased by 69.8%, 9.4%, and 60.2%, respectively. The balanced improvements were attributed to the increased crosslink density and fractional free volume as well as the unique inhomogeneous network structure because of incorporation of hyperbranched modifiers with proper structure and loading contents. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015, 132, 41910.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.