Abstract
ABSTRACTLead-free, piezoelectric (Na,K)NbO3-BaZrO3-(Bi,Li)TiO3 films were epitaxially grown onto (100) SrTiO3 substrate via pulsed laser deposition. The effects of post-annealing temperature on the crystal phases, mosaic spread, and chemical composition of the deposited (Na,K)NbO3 and (Na,K)NbO3-BaZrO3-(Bi,Li)TiO3 films were analyzed. Results indicate the epitaxial growth of (Na,K)NbO3-BaZrO3-(Bi,Li)TiO3 films deposited at an oxygen pressure (PO2) of ≥40 Pa and substrate temperature (Ts) of 800°C. The alkaline-deficiency could be suppressed in the (Na,K)NbO3-BaZrO3-(Bi,Li)TiO3 films deposited at PO2 ≥ 70 Pa. AFM profile of the (Na,K)NbO3 post-annealed at 1000°C indicates the epitaxial growth of film with atomically flat step-terrace structure, while that of the (Na,K)NbO3-BaZrO3-(Bi,Li)TiO3 film post-annealed at 1200°C shows relatively smooth surface with step-terrace structure and several cubic crystals. It was also found that the preferential evaporation of alkaline components could be suppressed by annealing under covered substrate condition.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.