Abstract
Abstract Epitaxial Cu2ZnSnSe4 (CZTSe) thin films have been grown via high temperature coevaporation on GaAs(001). Electron backscattering diffraction confirms epitaxy in a wide compositional range. Different secondary phases are present in the epitaxial layer. The main secondary phases are Cu2SnSe3 and ZnSe which grow epitaxially on top of the CZTSe. Transmission electron microscopy measurements show that the epitaxial CZTSe grows predominantly parallel to the c-direction. Epitaxial CZTSe solar cells with a maximum power conversion efficiency of 2.1%, an open-circuit voltage of 223 mV and a current density of 16 mA/cm2 are presented.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.