Abstract
The current–voltage and breakdown characteristics of Au/Ni/β-Ga2O3 Schottky barrier diodes were investigated as a function of β-Ga2O3 epilayer thickness in the range of 6–19 μm. The X-ray rocking curves indicated that the full-width half-maximum is reduced with increasing epilayer thickness, implying an improvement in the crystallinity of β-Ga2O3 epilayer. The barrier heights of the field-plated β-Ga2O3 Schottky barrier diode with epitaxial layer thickness of 6, 12, and 19 μm were obtained as 1.01, 1.03, and 1.04 eV, with the ideality factor values being 1.21, 1.19, and 1.46, respectively. The higher ideality factors could be associated with the existence of inhomogeneity at the metal–semiconductor interface. The series resistance of the Schottky diode obtained increased with increasing epilayer thickness. The Schottky diode fabricated on 19 μm thick epitaxial layer exhibited a higher breakdown voltage of 490 V. The increase in epilayer thickness led to the widening of depletion region, resulting in lower electric field over a larger distance. This could be a main cause of the enhancement of the breakdown voltage characteristics of β-Ga2O3 Schottky barrier diode.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.