Abstract
Abstract A yellow inorganic ceramic pigment with general formula Y1.86−xMxTb0.14O3−x/2 (M = Ca and/or Zn) with x = 0.06, 0.32 and 0.64 were synthesized by a modified Pechini method. XRD, SEM and HRTEM/EDX analysis showed the formation of solid solution at 1300 °C when x = 0.06 and 0.32. The best b* yellow coordinates were obtained for Ca and Zn co-doped Y1.86Tb0.14O3 samples. The intensity of the yellow colour in the samples is related to the presence of Tb4+ ions. Samples with higher concentration of Tb4+ ions lead to a better yellow colour. The chemical stability of these pigments was determinate in an industrial glaze. The glazing tests indicated that the powder samples with x = 0.06 and 0.32 fired at 1300 °C were stable in the glaze. These results make it a potential candidate for environmental friendly yellow ceramic pigment to be used in applications such as pigment for glazes or inkjet printers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.