Abstract
The residual mechanical properties of epoxy-organoclay nanocomposites after moisture and UV exposure have been evaluated. The flexural modulus decreased after moisture saturation, with much less extent for the nanocomposite than the neat epoxy. The tensile failure strain was significantly reduced with UV exposure time due to the embrittlement effect, and the addition of organoclay mitigated the failure strain reduction. The elastic modulus varied little with UV exposure time regardless of organoclay, because the modulus was determined by the core material which was unaffected by UV exposure. The microhardness and the modulus of the surface material determined from nanoindentation tests increased after UV exposure, with less extent in the nanocomposite than the neat epoxy due to the thinner embrittled top layer for the nanocomposite. All these observations confirmed the beneficial effects of organoclay in improving the barrier characteristics against UV exposure.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.