Abstract
Bi2Te3-based thin films are gaining recognition for their remarkable room temperature thermoelectric performance. Beyond the conventional "process-composition-performance" paradigm, it is highly desirable to explore new methods to enhance their performance further. Here, we designed a sandwich-structured Ag/PZT/PVDF/Bi0.5Sb1.5Te3(BST) thin film device and effectively regulated the performance of the BST film by controlling the polarization state of the PZT/PVDF layers. Results indicate that polarization induces interlayer charge redistribution and charge transfer between PZT/PVDF and BST, thereby achieving the continuous modulation of the electrical transport characteristics of BST films. Finally, following polarization at a saturation voltage of 3 kV, the power factor of the BST film increased by 13% compared to the unpolarized condition, reaching 20.8 μW cm-1 K-2. Furthermore, a device with 7 pairs of P-N legs was fabricated, achieving a cooling temperature difference of 11.0 K and a net cooling temperature difference of 2.4 K at a current of 10 mA after the saturation polarization of the PZT/PVDF layer. This work reveals the critical effect of introducing ferroelectric layer polarization to achieve excellent thermoelectric performance of the BST film.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.