Abstract
In the recent search nickel superalloy Inconel 600 was coated with Zr-modified aluminide diffusion coating using pack cementation technique. Diffusion coating was done in a single step utilizing a conversion reaction of 10% Al, 2% ZrO2, 4% NaCl, and 84 percent Al2O3 (wt. percent ) and a simultaneous aluminizing-zirconizing process. The diffusion coating operations were performed in an argon environment at 1050 °C for 10 hours. The test of the isothermal oxidation in dry air was performed on the Inconel Alloy 600 (IA600) without and with Zr-modified aluminide coating for 800-1000 °C. The oxidation kinetic of IA600 and its coated system was found to follow the parabolic law. The activation energy is 243 kJ/mol. for the coated system and 457 kJ/mol. for the uncoated system. XRD analysis show that oxide phases are formed on an uncoated IA600 surface during most of the oxidation exposure conditions are NiO, Cr2O3, Fe2O3, NiCr2O4 and NiFe2O4, , whereas alumina scale is the major oxide that is obtained on the surface of coated samples.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.