All-inorganic perovskite quantum dots have wide application prospects in the fields of lighting and display. However, the photoluminescence quantum yields of violet-blue emission for the CsPbCl3 quantum dots is still low. In this work, the Rb+ ions were successfully incorporated into the lattice of CsPbCl3 quantum dots with partially substituting the sites of Cs+ ions by the modified hot injection method. It was interesting to observe that the photoluminescence quantum yields of CsPbCl3 quantum dots was improved from 5.7% to 13% through the optimization of Rb+ doping concentration. The absorption and emission peaks of CsPbCl3 quantum dots shifted to blue, originating from lattice substitution of Cs+ with Rb+. Further investigation on the photoluminescence dynamics of the quantum dots revealed that the enhanced photoluminescence quantum yields resulted from the reduced defects in CsPbCl3:Rb quantum dots. This work offers a new approach to improve the optical performance of perovskite quantum dots.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.