Abstract
This work tries to improve the durability of electrocatalysts of gas diffusion electrodes (GDEs) by using multi-walled carbon nanotube supported Pt–Pd bimetallic (Pt–Pd/MWCNT). The durability investigation of multi-walled carbon nanotube supported metals was evaluated by a repetitive potential cycling (RPC) corrosion test and by extended constant potential (ECP) experiments. Potential cycling tests were performed from −0.3 to 1.2 V at 50 mV s −1 in 1 mol L −1 H 2SO 4. Extended constant potential (ECP) durability test were also carried out on the GDEs by 30 h of constant potential operation at 0.8 V vs. Ag/AgCl. The smaller performance loss was observed on the GDE using Pt–Pd/MWCNT as electrocatalyst compared with GDE using Pt/MWCNT during both durability tests. ICP analysis also suggests that the dissolution of Pt nanoparticles from the carbon nanotube surface is hindered when Pd is present.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.