Abstract
Some defects of polylactic acid (PLA), especially its poor mechanical properties, were modified using a minimum content of non-biodegradable maleated polypropylene (MAPP). To this end, first, the amount of MAPP was optimized, which was 20 wt.%. Second, MgO was used as a new catalyst to improve the exchange reactions between active groups in both polymers in a reactive blending process. Tensile and izod analyses showed that, compared to neat PLA, with a slight decrease in modulus and tensile strength, elongation at break, and impact resistance were improved in the presence of 20 and 0.1 wt.% of MAPP and MgO, respectively. This improvement in mechanical properties can be related to the exchange reactions between two polymers and the formation of PLA-MAPP block copolymers. MFI and WDCA analyses demonstrated the increase in melt flowability and surface hydrophilicity of the resulting blends, respectively. DSC analysis showed that the Tg values of both polymers approached each other in the presence of catalyst. Also, the elimination of cold crystallization of PLA and the decrease in the Tm and crystallinity of both polymers are clear reasons for the miscibility of the alloy. TEM displayed the proper dispersion of MgO nanoparticles within the polymer matrix, and in addition, the XRD test also proved the decrease in the crystallinity of both polymers and appropriate miscibility of the samples containing 20 and 0.1 wt.% of MAPP and MgO, respectively. These results can promise the design of a compound with the maximum amount of PLA for further use in various industries.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Polymer Analysis and Characterization
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.