Enhancing mechanical property and corrosion resistance of Al0.3CoCrFeNi1.5 high entropy alloy via grain boundary engineering

Abstract

In the present study, to improve the performances of Al0.3CoCrFeNi1.5 high entropy alloys (HEAs), grain boundary character distribution (GBCD) of Al0.3CoCrFeNi1.5 HEA has been optimized by an appropriate thermo-mechanical processing. The experiment results showed that the fraction of low-Σ coincidence site lattice (CSL) boundaries could reach approximately 80 % through cold rolling with deformation of 8 % and subsequent annealing at 1050 °C for 5 min. The reason for GBCD optimization could be attributed to sufficient strain-induced boundary migration (SIBM) or grain growth after recrystallization. While recrystallization is not favorable for optimizing GBCD. The mechanical properties and corrosion resistance have been enhanced, with a more pronounced improvement observed in the corrosion resistance. The corrosion current density icorr of the GBEM specimen stands at 0.23 μA∙cm−2, representing a reduction of 66 % in comparison to the BM specimen (0.68 μA∙cm−2). The improvement of corrosion resistance of Al0.3CoCrFeNi1.5 HEA resulted from the discontinuous random grain boundaries (RGBs) broken by the high fraction of low-ΣCSL boundaries, especially Σ3 boundaries suppressed the propagation of corrosion crack.