Abstract
Wire + arc additive manufacture (WAAM) was applied to produce INCONEL 718 superalloy (IN718) components in a layer by layer manner; further, interpass cold rolling was introduced to generate in-process thermomechanical processing effect during the deposition process. Mechanical testing showed that with rolling applied, the strength of the solution plus aging treated WAAM IN718 was improved from 1056 MPa (unrolled) to 1351 MPa (rolled) which met the wrought standard (1276 MPa), and the material anisotropy was eliminated. The unrolled IN718 featured large columnar grains developing along the building direction, with the length and width as large as 11 mm and 0.8 mm respectively; rolling induced plastic deformation triggered a non-uniform recrystallization upon successive depositions, which produced a recrystallized core with small columnar grains and numerous finely equiaxed grains with the grain size of 12.7 μm. The overall strengthening produced by interpass rolling was attributed mostly (76%) to the rolling induced recrystallization which produced grain size reduction strengthening and created larger grain boundary area to allow more precipitation at the grain boundaries, and partially (24%) due to the improved aging response of the recrystallized grain structure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.