Enhancing Mechanical and Corrosion Properties of AISI 420 with Titanium-Nitride Reinforcement through High-Power-Density Selective Laser Melting Using Two-Stage Mixed TiN/AISI 420 Powder.

Abstract

This study investigates the effect of laser volume energy density (VED) on the properties of AISI 420 stainless steel and TiN/AISI 420 composite manufactured by selective laser melting (SLM). The composite contained 1 wt.% TiN and the average diameters of AISI 420 and TiN powders were 45 µm and 1 µm, respectively. The powder for SLMing the TiN/AISI 420 composite was prepared using a novel two-stage mixing scheme. The morphology, mechanical, and corrosion properties of the specimens were analyzed, and their correlations with microstructures were investigated. The results showed that the surface roughness of both SLM samples decreases with increasing VED, while relative densities greater than 99% were achieved at VEDs higher than 160 J/mm3. The SLM AISI 420 specimen fabricated at a VED of 205 J/mm3 exhibited the highest density of 7.7 g/cm3, tensile strength (UTS) of 1270 MPa, and elongation of 3.86%. The SLM TiN/AISI 420 specimen at a VED of 285 J/mm3 had a density of 7.67 g/cm3, UTS of 1482 MPa, and elongation of 2.72%. The microstructure of the SLM TiN/AISI 420 composite displayed a ring-like micro-grain structure consisting of retained austenite on the grain boundary and martensite in the grain. The TiN particles strengthened the mechanical properties of the composite by accumulating along the grain boundary. The mean hardnesses of the SLM AISI 420 and TiN/AISI 420 specimens were 635 and 735 HV, respectively, which exceeded previously reported results. The SLM TiN/AISI 420 composite exhibited excellent corrosion resistance in both 3.5 wt.% NaCl and 6 wt.% FeCl3 solutions, with a resulting corrosion rate as low as 11 µm/year.