Abstract
Carbon fibre reinforced polymer (CFRP) composites based upon epoxy matrices containing polyethersulfone (PESU) and/or graphene nanoplatelets (GNPs) and/or multi-walled carbon nanotube (MWCNTs) were prepared by hand lay-up without any solvent. The influence of individual and hybrid toughened particles on flexural properties and mode I interlaminar fracture toughness were examined. The maximum value of normalised flexural strength (858 MPa) was measured for CFRP with PESU toughened epoxy. There are no noticeable changes in flexural modulus between all modified laminates. Mode-I interlaminar fracture toughness of crack initiation (GIc ini) and crack propagation (GIc prop) were enhanced when the matrices of laminates were toughened by whether thermoplastic or carbon-based nanomaterials. The epoxy laminates with 5 %wt PESU and a hybrid ratio of GNP/MWCNT 0.4/0.1 (%wt/%wt) exhibits the greatest GIc ini (228 J/m2) and excellent GIc prop (676 J/m2). Surface fracture revealed that this enhancement is due to the simultaneous toughening mechanism of PESU rich particles (crack deviation, crack pinning, debonding), GNPs (crack deviation), and MWCNTs (pull out). This work also evidences that it is important to introduce similar size of tougheners for improving interlaminar toughness of multifunctional CFRP composites.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.