Abstract
Background: Our previous study found that the addition of pentavalent cations like niobium (Nb) to yttria-stabilized zirconia increased fracture toughness but also raised the coefficient of thermal expansion (CTE), and opacity also increased undesirably. A new surface treatment is required to boost fracture toughness without altering CTE or translucency. Methods: The surfaces of pre-sintered 3 mol% yttria-stabilized tetragonal zirconia polycrystal (3Y-TZP) and 4.2 mol% yttria-stabilized partially stabilized zirconia (4.2Y-PSZ) were treated with a Nb sol solution containing Nb2O5 nanoparticles. After drying and sintering, a high-Nb-content surface layer formed with a depth of approximately 1 mm. Results: The Nb content in this surface layer matched that of a bulk material with 1 mol% Nb2O5. The tetragonality of the surface zirconia increased, enhancing the surface fracture toughness without changing the CTE or translucency. Conclusions: Adding Nb near the surface improved the fracture toughness without affecting the CTE or translucency. This method could strengthen zirconia prostheses, allowing more reliable dental restorations.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.